TEADIT style NA1122 was developed to exhibit superior thermal stability during extreme thermal cycling applications. It is specifically recommended for saturated and superheated steam services but has also proven itself to be very effective in sealing liquid petroleum derivates, ethanol, chemical products and other fluids. Field tests have validated the results found in our laboratories and have confirmed the higher performance capabilities of the NA1122 compressed sheet.
TEADIT style NA1122 is a compressed non-asbestos sheet gasket material produced from a combination of inorganic fibres and special fillers, bonded with nitrile rubber (NBR). It is manufactured through a hot calendar process under rigorous quality control standards that are registered under ISO-9001 certification. TEADIT style NA1122 is also available with wire reinforcement.
| Temperature (ºC) | Continuous Service: 430 |
| Maximum Service: 550 | |
| Pressure (bar) | Continuous Service: 102 |
| Maximum Service: 150 | |
| Availability (in mm) | 1.500 x 1.600 |
| 1.500 x 3.200 in | |
| Thickness (in mm) | from 0,4mm up to 3,2mm |
| Color | Black |
| Typical Physical Properties: | ||
|---|---|---|
| Density - ASTM F1315 | 1,6 g/cm3 | |
| Compressibility - ASTM F36A | 12-22% | |
| Recovery - ASTM F36A | 40% | |
| Tensile Strength Average - ASTM F152 | 9 MPa | |
| Thickness Increase - ASTM F146 - after 5hr | ||
| ASTM Oil IRM 903 @ 300ºF (150ºC) | 15% | |
| Fuel B, @ 77ºF (25ºC) | 15% | |
| Weight Increase - ASTM F146 - after 5hr | ||
| ASTM Oil IRM903 @ 300ºF (150ºC) | 30% | |
| Fuel B, @ 77ºF (25ºC) | 20% | |
| Torque Retention (DIN 52913) | 43MPa | |
TEADIT® Deutschland GmbH
Schanzenstraße 35, 51063 Köln, Germany
Phone: +49 (0)221/922 342-0
Fax: +49 (0)221/922 342-22
TEADIT® International Produktions GmbH
Rosenheimer Str. 10, A-6330 Kufstein Austria
Phone: +43-5372-64020-0
Fax: +43-5372-64020-20
2016 © Teadit | All Material Copyright are reserved.
This website uses modern technologies such as JavaScript, CSS, HTML5 and WebFonts; because of this, it is best viewed in modern browsers.
We recommend to use Google Chrome as your primary browser for this website.